F. Stadlbauer, T. Koch, F. Planitzer, W. Fidi, V. Archodoulaki:
"Einfluss des Rußfüllgrades von Elastomeren auf Aspekte der Ermüdung in Zug-Druck-Belastung";
Kgk-Kautschuk Gummi Kunststoffe, 66 (2013), 7-8; 37 - 42.

Corresponding to real elastomeric parts, this work focuses on investigating fatigue behaviour under tension-compression mode. Deviations in crack growth are taken into account by an extended measurement setup including shadow and fully illuminated images as well as images from the front and back side of the sample. Fatigue crack growth, fracture surfaces and heat build-up are measured for rubber samples loaded with different carbon black contents. The results show the reinforcing effect of carbon black, but also the presence of optimal carbon black filler content. The heat build-up is pronounced especially for highly filled samples.

In Anlehnung an reale Elastomerbauteile liegt der Fokus dieser Arbeit auf der Untersuchung des Ermüdungsverhaltens unter Zug-Druck-Beanspruchung. Mit Hilfe eines erweiterten Messaufbaus (Schattenbilder und voll beleuchtete Bilder, Bilder von der Vorder- und Rückseite der Probe) werden Abweichungen im Risswachstum berücksichtigt. Elastomerproben mit unterschiedlichen Rußfüllgraden werden hinsichtlich des Risswachstumsverhaltens, der Bruchoberflächen und der Eigenerwärmung untersucht. Es zeigt sich die verstärkende Wirkung von Ruß, aber auch das Vorhandensein eines optimalen Füllgrades. Die Eigenerwärmung ist vor allem für hoch gefüllte Proben sehr stark.

Ermüdung; Zug-Druck-Belastung; Rußfüllgrad; Eigenerwärmung