S. Großeiber, M. Rath, E. Kozeschnik:
"Modeling of the interaction between precipitate formation and forming - A thermo-kinetic approach";
Talk: MEFORM 2013, Altenberg; 2013-03-20 - 2013-03-22; in: "Simulation von Umformprozessen - MEFORM 2013", (2013), 69 - 78.

In the present work, two microalloyed steel grades are investigated experimentally in terms of their stress-strain curve and ductility behavior. One grade contains a comparably high density of precipitates. The particles, which do not directly contribute to precipitation strengthening due to their low volume fraction, impede dynamic restoration mechanisms (DRX and DRV). This, indirectly, leads to strengthening and a loss of ductility in the temperature region between 850 and 950°C. The mechanical behavior is finally correlated to the calculated precipitate distributions as evaluated with the thermo-kinetic models of the software MatCalc. Good agreement is observed between experiment and simulation.

In der vorliegenden Arbeit untersuchen wir experimentell das mechanische Verhalten zweier mikrolegierter Stähle hinsichtlich deren Spannungs-Dehnungs-Verhaltens und deren Duktilität. In einer Stahlgüte kommt es zu vermehrter Ausscheidungsbildung, welche sich behindernd auf die dynamische Erholung und Rekristallisation auswirken. Obwohl es zu keiner direkten Ausscheidungsverfestigung kommt, da der Phasenanteil dieser Teilchen zu klein ist, steigt die Festigkeit aufgrund der Ausscheidungen dennoch an und sinkt die Duktilität im Temperaturbereich von 850 bis 950°C. Dieses Verhalten wird schlussendlich erfolgreich mit berechneten Ausscheidungsverteilungen in Korrelation gebracht, welche mit den thermo-kinetischen Modellen der Software MatCalc ermittelt werden.