M. Nöhrer, W. Mayer, S. Zamberger, E. Kozeschnik, H. Leitner:
"Precipitation Behavior of Strain- Induced V Precipitates in Ferrite at Different Temperatures in a 0.2 wt% Carbon Steel";
Steel Research International, 85 (2014), 4; 679 - 688.

English abstract:
The evolution of strain-induced V precipitates at two different temperatures (600 and 700 degrees C) in ferrite was studied via atom probe tomography and transmission electron microscopy. The interpretation of experimental results is supported by simulation data, which was calculated by means of MatCalc. The study reveals that V carbonitrides are formed independently from the formation temperature. Initially, the precipitates have a higher N content than C. With longer dwell times, the C to N ratio changes from N- to C-rich V carbonitrides. At 700 degrees C formation temperature, the growth of precipitates and the change from higher N to higher C occurs faster than at 600 degrees C. Due to the faster growth, the V content in solid solution decreases earlier. The precipitates exhibit an elliptical shape and have NaCl type f.c.c structure. A [012]//[011](V(C, N)) and a [001]//[011](V(C, N)) orientation relationship with the ferrite matrix were detected.

"Official" electronic version of the publication (accessed through its Digital Object Identifier - DOI)

Created from the Publication Database of the Vienna University of Technology.