E. Aschauer, S. Sackl, T. Schachinger, H. Bolvardi, M. Arndt, P. Polcik, H. Riedl, P.H. Mayrhofer:
"Atomic scale investigations of thermally treated nano-structured Ti-Al-N/ Mo-Si-B multilayers";
Surface & Coatings Technology, 349 (2018), S. 480 - 487.

Kurzfassung englisch:
Mo-Si-B alloys came into the focus of research activities as an extremely creep resistant material for high
temperature oxidative environments. Here, we studied the mechanical, microstructural, and chemical changes of
physical vapour deposited protective Ti-Al-N/Mo-Si-B multilayer coatings during annealing in inert and oxidative
atmosphere (up to 1600 °C). We focused our investigation on morphological and structural changes of the
coating architecture, by applying a set of high-resolution techniques (e.g., high-resolution transmission electron
microscopy as well as atom probe tomography), in order to separate temperature or oxygen-induced effects on
the protective behaviour. The 31 nm thick Ti-Al-N layers crystallise in the preferred face centred cubic structure,
whereas the alternating Mo-Si-B layers are X-ray amorphous. Their thermomechanical properties, with a
hardness of at least 31 GPa of the film up to vacuum annealing temperatures of 1200 °C, are clearly superior to
homogeneously grown Ti-Al-N coatings. Applying X-ray powder diffraction, we observed that annealing in inert
atmosphere leads to the formation of the Mo-rich intermetallics T1-Mo5Si3 (A15, cP8,Cr3 Si-prototype) and T2-
Mo5SiB2 (D8l, tl32,Cr5B3-prototype), accompanied by the spinodal decomposition of Ti-Al-N. In contrast, exposing
this multi-layered coating to oxygen causes the formation of a rutile-TiO2 and α-Al2O3 oxide scale. The
presence of Mo-Si-B is evident up to temperatures of 900 °C, leading to a retarded oxidation process, where only
200 nm out of the 3.0 μm Ti-Al-N/Mo-Si-B multilayer is oxidised.

"Offizielle" elektronische Version der Publikation (entsprechend ihrem Digital Object Identifier - DOI)

Zugeordnete Projekte:
Projektleitung Paul Heinz Mayrhofer:
Christian Doppler Labors für anwendungsorientierte Schichtentwicklung

Erstellt aus der Publikationsdatenbank der Technischen Universität Wien.